疏水改性聚丙烯酸类增稠剂的合成

　　

疏水改性聚丙烯酸类增稠剂的合成

郭玉杰﹡

（青岛科技大学 橡胶材料与工程教育部重点实验室，山东 青岛 266042）

摘要：以α-甲基丙烯酸和多种丙烯酸酯类为原料，过硫酸钾（KPS）为引发剂，十二烷基硫酸钠和吐温-60为复配乳化体系，邻苯二甲酸二烯丙酯为交联剂，通过乳液聚合，合成出增稠剂。研究了甲基丙烯酸十八烷基酯（SMA）含量、交联剂用量、引发剂用量等因素对共聚物增稠剂增稠性能的影响。结果显示，单体配比是影响增稠剂各项性能的最主要因素，当SMA=1%时，增稠性能最好；随着交联剂的增加，耐盐性下降，增稠粘度先增大后减小，在交联剂为0.3%时出现最大值；引发剂量为0.3%时，所得聚合物的增稠性能最好，为0.4%时，所得聚合物的耐盐性最好。

关键词：疏水改性；丙烯酸；增稠剂；乳液聚合

Synthesia of Hydrophobically Modified Polyacrylic Acid Thickener

GUO Yu-jie*

(Key Laboratory of Rubber-plastics, Ministry of Education, Qingdao University of Science and Technology, Qingdao 266042, China)

Abstract: Thickener was prepared in the way of emulsion polymerization by using α-methyl methacrylate and variety of acrylate esters as raw materials , potassium persulfate (KPS) as initiator, sodium lauryl sulfate and tween -60 for the complex emulsion system, diallyl phthalate as crosslinker. Studied octadecyl methylester (SMA),crosslinker,initiator dosage impact on the properties of copolymer thickener thickening.The results show that monomer ratio is the most important factor which&nb

订阅方式：
①在线订阅（推荐）：www.sdchem.net.cn
②邮局订阅：邮发代号24-109

投稿方式：
①在线投稿（推荐）：www.sdchem.net.cn
　　作者只需要简单注册获得用户名和密码后，就可随时进行投稿、查稿，全程跟踪稿件的发表过程，使您的论文发表更加方便、快捷、透明、高效。
②邮箱投稿：sdhgtg@163.com sdhg@sdchem.net
　　若“在线投稿”不成功，可使用邮箱投稿，投稿邮件主题：第一作者名字/稿件题目。
投稿时请注意以下事项：
　　①文前应有中英文“题目”、“作者姓名”、“单位”、“邮编”、“摘要”、“关键词”；
　　②作者简介包括：姓名、出生年、性别、民族、籍贯或出生地、工作单位、职务或职称、学位、研究方向；
　　③论文末应附“参考文献”，执行国标GB/T7714-2005标准，“参考文献”序号应与论文中出现的顺序相符；
　　④注明作者的联系方式，包括电话、E-mail、详细的通讯地址、邮编，以便联系并邮寄杂志。
　　 　                                                                                   山东化工稿件修改细则