PU保温材料在空气中的热解特性研究

　　

摘要：运用热重-差热-红外-质谱联用(TG-DSC-IR-MS)技术研究了聚氨基甲酸酯（PU）在空气气氛下的热解特性。研究表明，PU在空气环境中热解主要有两个阶段，都属于放热过程。增大升温速率，热解向高温区移动，最大热解速率对应的峰值温度相应提高。PU热解过程首先是聚合物高分子长链断裂生成较短的链，之后氧气参与反应，主要分解产物有二氧化碳、水、碳和胺类、炔类、醇类、醛类物质。运用Ozawa-Flynn-Wall等转化率法求得活化能随转化率的关系曲线，得到活化能的平均值为152.9kJ/mol。

关键词：聚氨基甲酸酯；TG-DSC-IR-MS联用技术；热分解

Abstract: The thermal decomposition characteristics of polyurethane(PU) in air environment is studied by TG-DSC-IR-MS coupling technique method. The thermal analysis research indicated that there are two main weight loss processes during the thermal decomposition of polyurethane. With increasing heating rates, the initial and external temperature increases, and the maximum thermal decomposition rate corresponding to the peak temperature shiftes to a higher reaction temperature. When polyurethane is heated, the long chains break to shorter chains first, and then the shorter chains react with oxygen. The main products from the thermal decomposition of polyurethane in air are CO₂，C, amines, alkynes, alcohols, aldehydes. By Ozawa-Flynn-Wall method, the average activation energy of polyurethane is 152.9kJ·mol^-1.

Key words：Polyurethane；TG-DSC-IR-MS Coupling Technique；Thermal Decomposition

订阅方式：
①在线订阅（推荐）：www.sdchem.net.cn
②邮局订阅：邮发代号24-109

投稿方式：
①在线投稿（推荐）：www.sdchem.net.cn
　　作者只需要简单注册获得用户名和密码后，就可随时进行投稿、查稿，全程跟踪稿件的发表过程，使您的论文发表更加方便、快捷、透明、高效。
②邮箱投稿：sdhgtg@163.com sdhg@sdchem.net
　　若“在线投稿”不成功，可使用邮箱投稿，投稿邮件主题：第一作者名字/稿件题目。
投稿时请注意以下事项：
　　①文前应有中英文“题目”、“作者姓名”、“单位”、“邮编”、“摘要”、“关键词”；
　　②作者简介包括：姓名、出生年、性别、民族、籍贯或出生地、工作单位、职务或职称、学位、研究方向；
　　③论文末应附“参考文献”，执行国标GB/T7714-2005标准，“参考文献”序号应与论文中出现的顺序相符；
　　④注明作者的联系方式，包括电话、E-mail、详细的通讯地址、邮编，以便联系并邮寄杂志。
　　 　                                                                                   山东化工稿件修改细则