Zr-MFI分子筛的制备

　　

摘要:以正硅酸四乙酯为硅源，锆酸四丁酯为锆源，四丙基氢氧化铵为模板剂，采用水热法合成Zr-MFI分子筛。XRD、UV-Vis、FT-IR、TEM等手段表征载体的结构；考察了晶化时间、晶化温度和锆源变化对分子筛形成过程的影响。结果表明，晶化温度为170 ^oC，晶化时间为18 h有利于分子筛晶体的生成，合成的Zr-MFI分子筛具有五元环MFI结构。该分子筛为尺寸均一、分散性良好、直径约为240-280 nm的圆柱体；UV-Vis证实了Zr物种成功进入到分子筛骨架。我们将所得分子筛作为载体，通过负载纳米金颗粒制备催化剂Au/Zr-MFI，并将其应用于对硝基苯酚还原反应，该催化剂表现出良好的催化活性。

Abstract: Zr-MFI molecular sieves with different molar ratio of n(Si/Zr) were hydrothermally synthesized, using tetraethoxysilane and zirconium n-butoxide as silicon and zirconium sources, respectively, and tetrapropyl ammonium hydroxide as the template. The structure of the molecular sieve was characterized by XRD, UV-Vis and FT-IR. The influence of crystallization temperatures, crystallization time, and zirconium source on the final products was investigated. The results showed that the optimal crystallization of the molecular sieve was achieved at crystallization temperature 170 ℃ for crystallization time 18 h. Molecular sieve possesses MFI structure with five-membered ring. TEM analysis indicates that the molecular sieve is well-crystallized cylinder with diameter of 240-280 nm. UV-Vis characterization confirmed the entrance of Zr into the zeolite framework. Au/Zr-MFI molecular sieve catalysts for P-nitrophenol reduction exhibited better reaction acitivity.

订阅方式：
①在线订阅（推荐）：www.sdchem.net.cn
②邮局订阅：邮发代号24-109

投稿方式：
①在线投稿（推荐）：www.sdchem.net.cn
　　作者只需要简单注册获得用户名和密码后，就可随时进行投稿、查稿，全程跟踪稿件的发表过程，使您的论文发表更加方便、快捷、透明、高效。
②邮箱投稿：sdhgtg@163.com sdhg@sdchem.net
　　若“在线投稿”不成功，可使用邮箱投稿，投稿邮件主题：第一作者名字/稿件题目。
投稿时请注意以下事项：
　　①文前应有中英文“题目”、“作者姓名”、“单位”、“邮编”、“摘要”、“关键词”；
　　②作者简介包括：姓名、出生年、性别、民族、籍贯或出生地、工作单位、职务或职称、学位、研究方向；
　　③论文末应附“参考文献”，执行国标GB/T7714-2005标准，“参考文献”序号应与论文中出现的顺序相符；
　　④注明作者的联系方式，包括电话、E-mail、详细的通讯地址、邮编，以便联系并邮寄杂志。
　　 　                                                                                   山东化工稿件修改细则